Abstract

Laser-induced damage morphologies and the accumulation dependence of damage on single-crystal metal surfaces have been observed under Q-switched 1064-nm Nd:YAG laser irradiation at 10-nsec pulses. Several different damage morphologies were observed: slip-line formation, ripple patterns, flat melting, and boiling. Damage probability versus fluence curves and accumulation curves are plotted to investigate damage behavior as it correlates with morphology. Flat-melting damage was observed near the 50% damage fluence on chemically polished copper surfaces, and slip lines were found near the 50% damage fluence on electropolished aluminum surfaces. Surface defects produced during sample preparation greatly influenced the damage threshold of copper because of its high melting threshold. Accumulation curves showed different damage behavior for crystals of different orientation. Accumulation was the largest on (111) Cu and Al surfaces, and the single-shot damage threshold of these surfaces was less than the other crystal orientations for both Cu and Al. The threshold reduction in accumulation follows the equation F_N = F₁N^S−1, where F_N is the N-pulse damage threshold, N is the pulse number, and S is the slope of the accumulation curve. Accumulation appears to be the result of the storage cycle of thermal stress–strain energy induced by a laser pulse. The total strain energy induced by N laser pulses is proportional to N^1/3 for the measured values of S, which is 0.92.

© 1988 Optical Society of America

Predicting multipulse laser-induced failure for molybdenum metal mirrors

Michael F. Becker, Chunchi Ma, and Rodger M. Walser
Appl. Opt. 30(36) 5239-5246 (1991)

Pulsed laser-induced damage of metals at 492 nm

C. D. Marrs, W. N. Faith, J. H. Dancy, and J. O. Porteus
Appl. Opt. 21(22) 4063-4066 (1982)

Investigations on single and multiple pulse laser-induced damages in HfO₂/SiO₂ multilayer dielectric films at 1064 nm

Wenwen Liu, Chaoyang Wei, Jianbo Wu, Zhenkun Yu, Hui Cui, Kui Yi, and Jianda Shao
Opt. Express 21(19) 22476-22487 (2013)

Laser-induced damage studies in silicon and silicon-based photodetectors

V. K. Arora and A. L. Dawar
Appl. Opt. 35(36) 7061-7065 (1996)

Investigation of the laser-induced surface damage of KDP crystal by explosion simulation

Shengfei Wang, Jian Wang, Xiangyang Lei, Zhichao Liu, Jianfeng Zhang, and Qiao Xu
Opt. Express 27(11) 15142-15158 (2019)